Characteristics:
The RCZ temporary crown and bridge resins which have good weatherability and molding
stability. It is a non-skin irritation and non-skin allergy 3D printing photosensitive resin. It has the
characteristics of fast printing speed, high precision, and smooth surface of the finished product. The material
has ultra-high fracture resistance, bending resistance and high wear resistance. Its printed products have a
natural tooth look texture and the color is a translucent tooth color. It is ready to use after a simple surface
treatment and polishing. Suitable for mass-produced products such as temporary crowns, temporary bridges,
temporary teeth, invisible models, trial models for various dental and medical applications. Stable in oral
environment, odorless and tasteless.
Key Features:
Natural tooth appearance texture (A2 & A3 color)
High printing accuracy
High printing speed
High fracture and bending resistance
High mechanical strength
High wear resistance
Biocompatible
Apllication:
| Test item | Test standard | Value |
| viscosity | ASTM D445 | 500-600MPa·s-25℃ |
| Density | ASTM D792 | 1.12-1.15g/cm3-25℃ |
| color | N/A | A2, A3 color |
| Flexural modulus | ASTM D790 | 2500-2900 MPa |
| Bending strength | ASTM D790 | 110-120Mpa |
| Tensile Strength | ASTM D638 | 55-60Mpa |
| Tensile modulus | ASTM D638 | 2300-2800MPa |
| Elongation at break | ASTM D638 | 20%-30% |
| Notched Impact Strength | ASTM D256 | 80-110j/m |
| Shore hardness | ASTM D2240 | 80-85D |
|
Glass Transition temperature |
ASTM D3418 |
130℃ |
|
Heat Distortion temperature |
ASTM D648 | 135℃ |
|
Thermal Expansion coefficient |
ASTM D696 | 97*E-7 |
| Volume shrinkage | ASTM D955 | 3.56-3.96% |
| Linear shrinkage | ASTM D955 | 1.05-1.36 % |
|
Optimum storage temperature |
N/A | 20℃～25℃ |
| Curing wavelength | N/A | 355nm-405nm |
| Brand | RCZ |
|---|---|
| Types | A2, A3 |